PA66

ORACLE SFL10 RD(BK)is unreinforced, flame retardant Polyamide 66 resin for injection molding.elemental phosphorous and halogen free flame retardant PA66 This product is availible in reddish-brown and black colors TEST ITEMSTEST METHOD AND CONDITIONSTEST RESULTSTEST METHODUNITCONTITIONS(DRY)23DensityISO1183g/cm31.1Melt Volume RateISO1133cc/10min(275)2.16kg43.2Tensile StrengthISO527MPa10mm/min67.8Tensile strain at breakISO527%5Flexural ModulusISO178MPa2,800Flexural StrengthISO178MPa2mm/min82Charpy NotchedISO179KJ/m22.9m/s-1J11Izod Notched ImpactISO180KJ/m23.5m/s-1J8.6Flame resistanceUL-94V-0Processing GuidelinesMaterial Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficientTypical Profile Melt Temperature 250-280°C (482-536 °F) Mold Temperature 60-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate PA 66 nylon 66