Thermoplastischen Elastomer-PVC-Compound

Type and application TypeProductApplication and Cable Specification7006N70 oC Thermoplastic elastomer PVC insulating compound Insulating compound for flexible, mobile wires and cables of elevator and audio and etc. 7026N70 oC Thermoplastic elastomer PVC jacket compound Jacket compound for flexible, mobile wires and cables of elevator and audio and etc. 7326N70 oC Flame retardant thermoplastic elastomer PVC jacket compound Jacket compound for flame retardant, flexible, mobile wires and cables 9026N90 oC Thermoplastic elastomer PVC jacket compound Jacket compound for flexible, mobile wires and cables at 90 oC 0526N105 oC Heat resistant thermoplastic elastomer PVC jacket compound Jacket compound for heat resistant, flexible, mobile wires and cables at 90(105) oC Storage and transport Packaging25kg/bag, PE membrane inside bag and Kraft outside bag. Storage and transport: Avoiding in direct sunlight and weathering. The storage place should be in clean, cool, dry, and ventilated conditions. Properties Table ItemUnitStandard Value7006N7026N7326N9026N0526N Tensile Strength ≥ MPa 12.512.512.512.512.5 Elongation at Break ≥ % 300300300300300 Impact Brittleness Temperature oC -30-40-40-40-40Volume Resistivity, at 20 oC ≥Ωm 1.0×1091.0×1081.0×1081.0×1081.0×108Volume Resistivity, at 70 oC ≥Ωm 1.0×107 Dielectric Strength ≥ MV/m 1818181818 Hot Deformation ≤ % 6065656565Thermal Stability Time at 200 oC ≥ min 6060606080 Oxygen Index ≥ % 26 Thermal Aging Aging Temperature oC100±2100±2100±2120±2135±2 Aging Time h168168168168168 Tensile Strength after aging ≥ MPa 12.512.512.512.512.5 Variation on Tensile Strength % ±20±20±20±20±20 Elongation at Break after aging ≥ % 300300300300300 Variation on Elongation at Break % ±20±20±20±20±20 Shore Hardness A68±365±365±369±370±3 Elongating Shrinkage ≤ % 140140140140140