| Eigenschaft |
same dyeing abiliyt/dyeing way as acry... |
| Verwenden |
Spinning |
| Faserlänge |
102mm |
| Feinheitsgrad |
3D |
| Ort der Herkunft |
Jiangsu China (Mainland) |
| Marke |
HUAXIN |
| Grad |
Jungfrau |
convertedmodified polyester TOPS virgin made from polyester staple fiber(PSF),raw white,suitable toproduce worsted yarn blend with wool/acrylic fiber. Test ItemUnitGrade AAdenierden3cut lengthmm102mmTenacity at BreakCn/den>=3.3Crimp Numberpcs/25mm7.9-8.2Elongation%43.5shrinkage%12spinning finish%0.14Electricity ResistanceΩ.cm1.24*0.7weightgrams/m20deviation of weight %0.2moisture regain%1.5