PVDF und Polyester lackiertem Aluminium Verbundscheibe

AulandPVDF and polyester painted aluminimum composite panels are designed to meet the robust requirement of cladding for high rise buildings, as well as providing versatile decorative options for designers to create their own masterpiece. It has superior flatness, uniform color, excellent mecahncial propertiesand absolute confirmity to fire retardant properties. Apart from the standard colors, metallic silver, silver grey, pure white, champagne silver, red, yellow, blue etc, customer can select colors from Pantone and RAL lists. We also accept orders with colors matching customer provided Aluminium plastic composite panel. Auland aluminum composite panels are composed of plastic core of low density and high density polyethylene laminated at both sides by two skins of 0.5mm or less aluminum sheets. The surface is painted either with polyester or Polyvinylindene Difluoride paint suitable for indoor and outdoor decoration. They are widely used in various applications, such as cladding,indoor decorative wall, cabinet cover, signage board, ceilings, decorative door etc. Apart from the abovementioned product,there are other product series available from us, includingEmbossed PEseries for indoor decoration, Brushed PE and PVDF series forindoor and outdoordecoration, Marble alike film laminated series, Crown series for high tech and glamorous decoration, High gloss pearly bright colorful film laminated series for indoor decoration, pre-anodized series for high reflection decorative requirement, marble/wood alike PVDF coated series for outdoor patterned decoration etc. Our product are designed and manufactured to meet the international standard with some technical details highlighted below. General Specifications Thickness 3mm,4mm,5mm,6mm (+/- 0.2mm) Width 1220mm,1250mm,1500mm (+/- 2mm) Length Less than 6000mm (+/- 4mm) Physical properties Standard Measurement Panel wight ASTM D-792 T3mm=4.6kg/m² t4mm=5.5kg/m² Thermal expansion ASTM D-696 3X 10¯5/°c Thermal conductivity ASTM C-519 0.39 kcal/m.hr°c (4mm) Deformation temperature ASTM D-648 115°c Mechanical roperties Standard Measurement Tensile Strength ASTM D-638 49Mpa Yield Strength ASTM D-638 44Mpa Bending Strength ASTM D-790 120Mpa(4mm) Flexural Elasticity ASTM D-790 2.6X10000Mpa(4mm) Shearing Strength ASTM D-732 33 Mpa Penetrating ResistanceASTM D-732 11 KN Adhesive Peel Off Strength ASTM D-903 10N/mm Wind Pressure resistance ASTM D-330 Passed Resistance against water ASTM D-331 Passed Resistance against air ASTM D-283Passed Auland PVDF Coated Composite Panel Techical Data Dry film AAMA2605-98 7.4.1.1 ASTM 3359,Method 8,100%, no change Wet film AAMA2605-98 7.4.1.2 37.8°c,24 hrs, 100%,no change Boiling water AAMA2605-98 7.4.1.3 100°c,20mins,100%, no change Impact Resistance AAMA 2605-98 7.5.4 No crack,100% adhesion,@3mm(±0.3mm) Abrasion Resistance ASTM D-968-93 No change Alkaline Resistance ASTM D-1308-87 No bubble,no change Acid Resistace ASTM D-1308-87 No change Mortar Resistance AAMA 2605-02-7.7.2 No change Detergent Resistance ASTM D-2248-93 No change Humidity Resistace ASTM D-2247-94 3000 hrs, 100% RH,38°c,no change Salt Spray ASTM B-117-90 No change Color Retention ASTM D-2244-93 Max 5 units after 4000 hrs Chalk resistance ASTM D-4214-89 Max 8 units after 4000hrs Gloss retention ASTM D-523-89 70% after 4000 hrs Corrosion resistance ASTM B-244 5%