| Eigenschaft |
even |
| Verwenden |
Spinning |
| Faserlänge |
88MM 102MM |
| Feinheitsgrad |
3D |
| Ort der Herkunft |
Jiangsu China (Mainland) |
| Marke |
huaxin |
| Modell-Nummer |
1.5D* 88MM |
| Stil |
Solid |
| Grad |
Recycling |
TOPS regeneratedconverted from tow,dope dyed,suitable toproduce worsted yarn blend with wool/acrylic fiber. Test ItemUnitGrade AAdenierden3cut lengthmm102Tenacity at BreakCn/den>=3.0Crimp Numberpcs/25mm10Elongation%27-48shrinkage%,180C,30mins8spinning finish%0.14Electricity ResistanceΩ.cm1.24*0.7weightgrams/m20deviation of weight %0.2scatter modulus%16.27