Polyamid 66

ORACLE TM 6030G is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability TEST ITEMSTEST METHOD AND CONDITIONSTEST RESULTSTEST METHODUNITCONTITIONS(DRY)23DensityISO1183g/cm31.4Melt Volume RateISO1133cc/10min(275)2.16kg9.6Tensile StrengthISO527MPa10mm/min180.4Tensile strain at breakISO527%5Flexural StrengthISO178MPa260Flexural ModulusISO178MPa8,000Charpy NotchedISO179KJ/m22.9m/s-1J21Izod Notched ImpactISO180KJ/m23.5m/s-1J20.9Flame resistanceUL-94HBAsh content%33.5Processing GuidelinesMaterial Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficientTypical Profile Melt Temperature 270-305 °C (518-581 °F) Mold Temperature 70-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate We direct our energies to offer users the high-performance, consistent-quality ,cost-saving nylon.Eachbatchhave to pass strict test before they go out . ORACLE provide six series polyamides resin to serve users a wide range of needs. >>> General Purpose Homopolymer >>> Reinforced nylon resin(Glass-reinforced and/or Mineral-reinforced) >>> Flame Retarded >>> Friction&Wear resistance >>> Impact resistance >>> Special applications Contactus forfurther information, general guides and/or additional information about ventilation PA66