PA66 Resin - flammwidrig

ORACLE 60Fis a kind of environment protectionPA66 material improved flame retardance and enhanced long-term performance. Flame retardant based on nitride ; outstanding mechanical and electrical properties. TEST ITEMSTEST METHOD AND CONDITIONSTEST RESULTSTEST METHODUNITCONTITIONS(DRY)23DensityISO1183g/cm31.1Melt Volume RateISO1133cc/10min(275)2.16kg43.2Tensile StrengthISO527MPa10mm/min67.8Tensile strain at breakISO527%5Flexural ModulusISO178MPa2,800Flexural StrengthISO178MPa2mm/min82Charpy NotchedISO179KJ/m22.9m/s-1J11Izod Notched ImpactISO180KJ/m23.5m/s-1J8.6Flame resistanceUL-94V-0Processing GuidelinesMaterial Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficientTypical Profile Melt Temperature 250-280°C (482-536 °F) Mold Temperature 60-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate We direct our energies to offer users the high-performance, consistent-quality ,cost-saving nylon.Eachbatchhave to pass strict test before they go out . ORACLE provide six series polyamides resin to serve users a wide range of needs >>> General Purpose Homopolymer >>> Reinforced nylon resin(Glass-reinforced and/or Mineral-reinforced) >>> Flame Retarded >>> Friction&Wear resistance >>> Impact resistance >>> Special applications Contactus forfurther information, general guides and/or additional information about ventilation PS: ORACLE nylon products aremainly usedto makehigh quality and reliable products. we don't offer recycledor/and cheap and nastynylon material