| Ort der Herkunft |
Henan China (Mainland) |
| Al2O3-Gehalt |
55% |
| SiC-Gehalt (%) |
22% |
| Modell-Nummer |
ZSLT-A |
| Marke |
Peng Ju |
| Form |
Block |
| Material |
Siliziumkarbid (SiC) |
BodyTopAl2O3,(%) ≥5570F.C+SiC,(%) ≥2213ZrO2,(%) ≥----MgO,(%) ≥----Apparent Porosi(%) ≤1717Bulk Density(g/cm3) ≥2.42.6Cold Crush Strength(Mpa) ≥2526Modulus Of Rupture (Mpa) ≥78Thermal shock resistance ≥55Con-casting time10-12