Kupfer-Zink Hartlot Schweißdraht

Description Copper-Zinc Brazing Alloy are suitable for gas flame brazing ,high temperature brazing of copper and copper alloy, nickel, cast iron and hard alloys ,During oxy-acetylene brazing , to heat with oxidized flame quickly can lessen evaporation of zinc and prevent porosity from over-oxidization. The opromum joint gap is 0.025-0.1mm. Flux is also necessary to obtain good brazing seam. Product name AWS Grade EN 14640 Grade BS 1845 Chemical Composition Brass (copper-zinc) RBCuZn-A CuZn40 Cu 57-61,Sn0.25-1.0,Zn blance Brass (copper-zinc) CZ6A Cu 58.5-61.5,Sn0.2-0.5,Si 0.2-0.4 ,Zn blance Brass (copper-zinc) RBCuZn-B CuZn40Ni Cu 56-60,Sn0.8-1.1,Ni 0.2-0.8 ,Zn blance Brass (copper-zinc) RBCuZn-C Cu 56-60,Sn0.8-1.1,Fe 0.25-1.20,Zn blance Nickel Silver RBCuZn-D CuZn40Ni10 CZ8 Cu 46-50, Ni 9-11,Zn blance Filler Metal Diameter 1.6mm-5.0mm Rod length: 400mm,500mm,914mm,1000mm.ect. Size otherwise specified by customer request or mutual agreement.