Kantenband

edge banding tape 1.thickness:0.2 0.5mm 2.Tensile strength:2000N/cm 3.Breakdown voltage:adove 25 KV 4.SGS,RoHS,adhesive tape The fiber glass banding tapes are of high quality,which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin ,and manufactured with the proprietory technology which are transferred from VONROLL ISOLA of Italy . It's widely used in AC.DC motors ,generators and transformers especially in traction motors. Specification :type width (mm) thickness(mm) Put up H200-W H200-G-W H150-G-W 10.20.25.30.50±10%0.30±10%Spool or pancake Properties : unitH200-WH200-G-WF150-G-WThermal classHFVolatile content%not above : 2Loss of weight at calcination%26±2Soluble resin content%above : 90Tensile strength before curingN/cmabove:2000above :1500above :1000Maximum pull while bandingN/cm1000800800Tensile strength of ringlike sample at room temperature after curingMpa200cabove :1000above :900above :900Tensile strength of ringlike sample at working temperature after curingMpa2000c1800c1500cabove :700above :600above :560Proof tracking indexabove 500VArc resistanceSabove : 160Breakdown voltage parallel to layersKVnormal condition:adove 25 after soaked in water for 24 hours:above 10ThermosettingOKLoss of tensile strength after soaked in oilnot above:10% Curing condition (Time to bring the piece to the temperature is not considered)Temperature°C160150135120115Timehour2.53.05.014.020.0Storage StabilityStorage temperature°C10152030 timeH200-wmonth2418128H200-G-W F150-G- W2015106Standard spool or pancake sizeSpecial put ups are available upon request.