Industrielle Keramikrohre

99.7 9.95 alumina ceramics, is my company launched in early 2007, after the new product manufacturing process of glass-ceramics microcrystalline alumina ceramic tube euro-american. Japan, it's good user's appearance, strength, colour and lustre smooth porcelain pipe is 20 times. In oxidation atmosphere using automatic forming oxidation film, prevent corrosion, thermal shock resistance, good at 15-6 times no room temperature crack, long-term use of 165 degrees highest temperature 1850. Refractoriness 2055 degrees volume density 3.92. Breakdown voltage 15KV/MM, hardness, AL2O3 content's nine percent 99.7 99.5 - that use the product: must be preheated. Technical performance numerical value High aluminum Corundum Al2O3 content >85 99-99.5 SiO2 content <12 <0.2 Fe2O3 conten <0.5 <0.05 0.1 Using temperature Long-term1550 Short-term1600-1700 1600 The maximum use temperature 1600 1800 HardnessMohs 7 8-9 Densitykg/m3 slip casting 3.7-3.9 hot embossing 3.7-3.85 Water Absorption% <0.2 0.1 0.2 Rupture strength slip casting 2000Kg/ hot embossing 1500Kg/