Hao Bote Aluminiumlegierungsblech / Platte 5052-O-H112,5

The internationally accepted chemical composition for the 5052 aluminum alloy:GradeSiFeCuMnMgCrNiZnTiZrImputiryAl50520.40.400.100.40 1.04.0 4.90.05 0.25-0.250.15-0.15RestThe internationally accepted mechenical properities for the 5052aluminum alloy sheet:GradeTemperThicknessTensile StrengthElongtion StrengthElongtion RateBend Radius5052O> 0.20 0.50170 21565120t> 0.50 0.15140t>1.50 3.00160.5t>3.00 6.00181.0t>6.00 12.50192.0t>12.50 50.0018—Sth more about 5052:5052 is often referred to as "Anodize Quality Aluminum", as it has excellent finishing qualities and anodized coatings are bright and clear.5052 contain the alloying element which is magnesium in sufficient quantities to cause substantial lowering of the melting point without producing brittleness. When magnesium is used as the major alloying element, or in combination with manganese, the result is a moderate to high strength non-heat treatable aluminum alloy.5052 is of reasonable bend radii.5052 has good resistance to corrosion, especially in salt-water or marine atmospheres.5052 has the best welding characteristics (Weldability is very good)of all the aluminums.5052 is widely used for cooking utensils, food processing equipment, storage tanks, truck and trailer components, mail boxes, aircraft components, electronic chassis, boat hulls, deck houses, hatch covers, pressure vessels, ladders, railings, frames, drip pans, tool boxes, truck bumpers, inner and outer body panels and components in truck and auto industries, kitchen equipment, decorative trim, architectural uses, signage applications, and any number of parts and application requiring strength and good formability at reasonable cost.Sth more about ALUMINUM and the ALUMINUM ALLOY :light in weight, commercially pure aluminum has a tensile strength of about 13,000 psi. Cold working the metal approximately doubles its strength.In orer to increase strength, aluminum is alloyed with elements such as manganese, silicon, copper, magnesium, or zinc. The alloys can also be strengthened by cold working. Some alloys are further strengthened and hardened by heat treatments. At subzero tem, aluminum is stronger than at room tem and is no less ductile. Most aluminum alloys lose strength at elevated temperatures, although some retain significant strength to 500°F. Besides a high strength-to-weight ratio and good formability, aluminum also possesses its own anticorrosion mechanism. When exposed to air, aluminum does not oxidize progressively because a hard, microscopic oxide coating forms on the surface and seals the metal from the environment. The tight chemical oxide bond is the reason that aluminum is not found in nature; it exists only as a compound.Our moulds cover nearly all the specifications the customers need, base on the absolutely qualified mechanical properties. Pls just call me directly or chat online for more detail!