ABS

ABS is a kind of high strength, toughness, good thermal plastic forming of easy machining of polymer materials. Because of the high strength and corrosion resistance, high temperature resistant, itis often used in the manufacture of plastic casing. Technical Data Sheet PropertyUnitTestingmethodTestingconditionABS350CPhysicalpropertiesSpecific gravityg/cm3ASTM D792-1.19Melt flow rateg/10minASTM D1238200/5kg4g/10minISO 1133220/10kg40MechanicalpropertiesTensilepropertiesTensile strengthMPaASTM D63810mm/min44Elongation at break%ASTM D63810mm/min30FlexuralpropertiesFlexural strengthMPaASTM D7905.4mm/min66Flexural modulusMPaASTM D7905.4mm/min2100IZODIZOD impact valueKJ/m2ASTM D256231/830ThermalpropertiesDeflection temperature under loadoCASTM D6481.82MPa72 oCASTM D648Annealed 80/4h; 1.82MPa88Molding shrinkage rate%----0.3%-0.5%Flame retardance-UL 941.6mmV0