Schamottemörtel (AL-40, 45) Refractory MortarsFireclay refractory mortarRefractory castable and refractory mortar supplier HENAN XINMI CHANGXING REFRACTORYCo., Ltd is the specia
Versorgung großer Qualität von Mullit Mortar (AL-80) Mullite MortarMulite Refractory Refractory MortarUnshaped Refractories manufacturer HENAN XINMI CHANGXING REFRACTORY Co., Ltd is the specialized manu
Schamottestein für heißen Ofen verwendet Phydical and chemical indicators offireclay bricks used for hot stove ItemsParametersRN-42RN-40RN-36AL2O3% ≥424036Refractability CN.0.2 Mpa the st
feuerfeste Ziegel für Kokerei Clay bricks for coke oven battery itemsindexN-1N-2aN-2bN-3aN-3bN-4N-5N-6Refractoriness,cone CN 1761741741721721701661581400135013201300Linear change%
feuerfeste Ziegel für Hochofen itemsindexZGN-42GN-42Al2O3%42 min42 minFe2O3%1.6 max1.7 maxrefractoriness176176refractoriness under load at 0.2Mpa1450 min1480 minpermanent linear ch
feuerfest itemsindexAl2O3%75 minSiO2%23 maxFe2O3%0.5 maxApparent porosity,%17 maxCapacity2.57 g/cm minRefractoriness under load T0.51670oC minCold crushing str
feuerfest itemsAl2O
hohe Tonerde Ziegel itemsindexGL-65GL-55GL-48Al2O3%65 min55 min48 minFe2O3%2.0 maxrefractoriness180178176refractoriness under load at 0.2Mpa1500 min1480 min1450 minperma
Ziegel caly brick for glass furnace pls check the physical and chemical indicators itemsindexBN-40aBN-40bAl2O3 %40Fe2O3 %1.5 max1.8 maxrefractoriness under
Silica Mörtel itemsindexJGN-92JGN-85refractoriness,cone number166158modulus of rupture Mpa 110oC drying 1400oC*3h after burning1.0 min 3.0min1.0 min 3.0minbonding
Tonziegel für Kokerei Clay bricks for coke oven battery itemsindexN-1N-2aN-2bN-3aN-3bN-4N-5N-6Refractoriness,cone CN 1761741741721721701661581400135013201300Linear change%
Tantalstab WearefactoryspecializinginthemanufactureandexportTantalum and Niobium prodcut formorethantenyears. we can provide many forms as follows Tantalum rod
SwagedTungsten Ruten / Rods Gestreckte nach Draw ProductsSize we can supply Tungsten rod Dia.1.5 - 100 mm, Length: 1000 mm max, Weight: 50 kgs. Tungsten tube O.D.3.0 - 380 mm, Length: 500 mm max, Wa
Wolframschwerlegierungen-Ringe heavy alloys(WNiFe, WNiCu) consist of 85-98% tungsten with balanced commonly nickel and iron or copper. The alloys are made by liquid-phase sintering
Molybdän Bleche, Platten und Folien Tungsten platestungsten rods and tungsten crucibles ContentPure tungsten ( W 99.95% );Tungsten PlatesProcessSintering, Forging, Rolling and Machining
Boden Molybdändraht 1 molybdenum wire Type & Applications: TypeApplicationMo1Applied for making mandrel, side rod, support, lead, etc.MoGApplied for making support,
Wolframschwerlegierungen Blätter heavy alloys(WNiFe, WNiCu) consist of 85-98% tungsten with balanced commonly nickel and iron or copper. The alloys are made by liquid-phase sintering
Hochwertige Feuerziegel . QN-JM26fire brick 1.Bending strength :1.1Mpa 2.Lower content in iron, alkaline and impurities, good high temperature properties, energy goodresista
Hochwertige feuerfesten Ankern refractory anchor: 1.40 years experience 2.Possess invention patent certificate. 3.Used for petrochemical,kiln industry etc. 4.Properties and pricing
QN-23 Hochwertige Feuerfeststein QN-JMinsulation brick 1.Thermal conductivity w/m .k (400°c) 0.15. 2.Lower content in impurities. 3.Safty application temperature:1260 °c. 4.B
Hochwertige Feuerziegel . QN-JM26fire brick 1.Bending strength :1.1Mpa 2.Lower content in iron, alkaline and impurities, good high temperature properties, energy goodresista
Hochwertige Feuerziegel . QN-JM26fire brick 1.Bending strength :1.1Mpa 2.Lower content in iron, alkaline and impurities, good high temperature properties, energy goodresista
Hochwertige Feuerziegel . QN-JM26fire brick 1.Bending strength :1.1Mpa 2.Lower content in iron, alkaline and impurities, good high temperature properties, energy goodresista
Zirkonia Dimensionierung Düsenblock zur Stahlherstellung Zirconia sizing nozzle block 1.40 years experience 2.ZrO2 65%-95% 3.Used for steel-making 4.Exported to USA,JAPAN,etc. Zirconia Sizing Nozzle BlockT
QN-JM-30 Patentfeuerfeste Schamottestein QN-JM-30 Refractory fire brick 1.Thermal conductivity w/m .k (400°c) 0.41. 2.Lower content in impurities. 3.Safty application temperature:1650 De
Tungsten Boote Specifications: 1) Material: W 99.95% (min.) 2) Shiny surface 3) Size: according to users' drawings 4) Standard sizes: 308, 310, 315, 215, 413, 52
Wolfram Sputtertargets W sputter target Specifications: 1) Material: W 99.95% (min.) 2) Shiny surface 3) Fine grain size 4) Density : 19.0 g/cm3 min 5) Maximum Size: Thick
Tungsten Alloy Rods Tungsten Alloy Rod: Materials: WNiFe, WNiCu As per AMS-T-21014 Density : 17.0 - 18.5 g/cm3 Hardness: 20 - 35 HRC Size : dia.3 - 350 mmx 20 - 550 mm l
Copper Tungsten Rods Copper tungsten rod ( WCu rod ) Specifications: 1) Copper tungsten alloy rod and plate 2) Materials: 70%W/Cu, 75%W/Cu, 80%WCu, 90%WCu 3) Technique: i
Keramikkern 1 FILTEC® EC85 Ceramic Cores is a high silica product with intermediate particle size distribution, it is made by unique technology at FILTEC's ISO
EC85 Keramikkerne FILTEC® EC85 Ceramic Cores is a high silica product with intermediate particle size distribution, it is made by unique technology at FILTEC's ISO
feuerfeste Steine zur Auskleidung Ofen Pfannenofen High Alumina Bricks for steel ladle and the cover of electric stoveItemsHigh Alumina Bricksfor steel ladleMicro-expansionfor steel ladleBurned High A
säurebeständige Ziegel für Beiztank Nut fl Data sheet of the products ItemSpecificationTest methodPhysical propertyRefractoriness ≥1710GB/T7322-87Bulk density g/cm3≥2.1GB/T2997-82Aparant
hohe Tonerde Ziegel für Futter Ofen Pfanne furnac High Alumina Bricks for steel ladle and the cover of electric stoveItemsHigh Alumina Bricksfor steel ladleMicro-expansionfor steel ladleBurned High A
Feuerfest Silikasteinen für Kokerei Spec. Typical value Chinese Test standard AL2O3 % 0.9 GB/T 6900 Fe2O3 % 0.8 Bulk Density g/cm3 1.8 GB/T2997-2000 Apparent Porosity % 23 GB/T2997-200
leichte Isolierung Feuer-Ziegelstein für die Verkleidung ove LBK23LBK26LBK28LBK30Bulk density (g/cm3)≤0.55≤0.68≤0.75≤0.85Cold crushing strength Mpa≥1.0≥1.5≥2.0≥2.5MOR MPa≥0.8≥1≥
Mullit Wärmedämmziegel für Ofen Ofen lini LBK23LBK26LBK28LBK30Bulk density (g/cm3)≤0.55≤0.68≤0.75≤0.85Cold crushing strength Mpa≥1.0≥1.5≥2.0≥2.5MOR MPa≥0.8≥1≥
feuerfeste Isolierung gießbaren The specificationofcastablecan be made as per the requried. INSULATION CASTABLE MAXIMUM WORKING TEMPETUREC10001250Bulk densityg/cm30.851.7Cold crus
feuerfest The specification and brick shape can be made as per the requried
Mullit Ziegel für Unterlauf Stahlguss Spec. Stardand value Typical value Chinese Test standard AL2O3 % >68 70 GB/T 6900 Fe2O3 % <1.8 1.3 Bulk Density g/cm3 >2.3 2.34 GB/T2997-20
extrudierten batt The extruded batts could be used to different kiln for sanitaryware, bone china, crystallized glass panel, bricksandroof tile. The max using temperat
Ziegeldach we are the maunfauter of mullite-cordierite kiln furniture, which max using temperature is 1300 degree. The length of hanging rail is adopted accordi
Loch batt The mullite-cordierite holes slab has an excellent thermal shock resistance; high hot MOR, no contamination of products during usage, and can be used
Plain Platte We could press batt according to customer's requirements. The max. dimensions are 1m x 1mm x 28mm. The max. usage temperature is 1,350°C
extrudierte Vliese We can supply different sizes of cordierite hanging rails and hanging cranks for different kilns. The max. usage temperature is within 1350°C. It
feuerfeste Hocker The stool is made of mullite-cordierite, which max using temperature could be 1300 degree. The product has an excellent thermal shock resistance, hig
Rollbackstein The cordierite brick could be used to roller kiln , which max use temperaturing is 1350 degree
Cordierit-Brennkapsel
Kalzinierten Bauxit Calcined Bauxite ITEMAL-1AL-2 AL-3 AL-4 AL-5 AL-6 Al2O3(% MIN.)8887 86 85 80 75 Fe2O3(% MAX.)1.8 2 2 2 2.5 2.5 TiO2(% MAX.) 4 4 4 4 4 4SIO2(% MA
Flint Lehm Flint Clay Chemical Analysis AL-1 AL-2 AL-3 AL-4 AL-5 AL-3 AL2O3 (%) 40-45 42-45 43-45 44-46 45-47 45-48 FE2O3 (%, MAX.) 3.5 2.5 2.0 1.5 1.5 1.2 B.D