PA6 30%GF

ORACLE TMD V30T NCis 30% Glass fiber reinforcedPA6 with outstanding impact resistance for injection molding grade It has good mechanical properties,used in all infustrial sectors, where reinforced materials are required to satisfy the part requirement TEST ITEMSTEST METHOD AND CONDITIONSTEST RESULTSTEST METHODUNITCONTITIONS(DRY)23DensityISO1183-87g/cm31.36Melt Volume RateISO1133cc/10min(275)2.16kg4.4Tensile strengthISO527MPa145Tensile strain at breakISO527%6Flexural StrengthISO178MPa183Flexural ModulusISO178MPa7,000Charpy NotchedISO183-93KJ/m22.9m/s-1J25Heat distortion temperatureISO75-931.8Mpa26Flame resistanceUL-94HBGlass fibre content%33.8Processing GuidelinesMaterial Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficientTypical Profile Melt Temperature 240-260 °C (464-500 °F) Mold Temperature 60-90 °C (140-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate We direct our energies to offer users the high-performance, consistent-quality ,cost-saving nylon.Eachbatchhave to pass strict test before they go out . ORACLE provide six series polyamides resin to serve users a wide range of needs. >>> General Purpose Homopolymer >>> Reinforced nylon resin(Glass-reinforced and/or Mineral-reinforced) >>> Flame Retarded >>> Friction&Wear resistance >>> Impact resistance >>> Special applications Contactus forfurther information, general guides and/or additional information about ventilation PS: ORACLE nylon products aremainly usedto makehigh quality and reliable products. we don't offer recycled& cheap and nastynylon material