尼龙6轮胎结构的脐带

ItemsUnit930dtex/21400dtex/21870dtex/22100dtex/2(840 D/2)(1260 D/2)(1680 D/2)(1890 D/2)Breaking StrengthNMIN 135MIN 208MIN 275MIN 310Elongation at Load%9.5±0.89.5±0.89.5±0.89.5±0.8(4.5KG)(6.8KG)(9KG)(10.2KG)Adhesion(H-Test)N/CMMIN 107.8MIN 137.2MIN 156.8MIN 166.6Unevenness Of Strength%MAX 5.0MAX 5.0MAX 5.0MAX 5.0Unevenness Of Elongation At Break%MAX 7.5MAX 7.5MAX 7.5MAX 7.5Cord GaugeMM0.55±0.040.65±0.040.75±0.040.78±0.04TwistZ twistT/CM460±15370±15330±15320±15S twist460±15370±15330±15320±15Dip Pick Up%4.5±1.04.5±1.04.5±1.04.5±1.0Elongation At Break%22±223±223±223±2Moisture Content%MAX 1.0MAX 1.0MAX 1.0MAX 1.0Heat Shrinkage%MAX 8.0MAX 6.5MAX 6.5MAX 6.5Fabric WidthCMM±2M±2M±2M±2ItemsUnit930dtex/11400dtex/11870dtex/1(840 D/1)(1260 D/1)(1680 D/1)Breaking StrengthNMIN 67MIN 98MIN 127Elongation at Load%7.5±1.07.0±1.08.0±1.0(2.3KG)(3.4KG)(4.5KG)Adhesion(H-Test)N/CMMIN 49MIN 64MIN 78Cord GaugeMM0.32±0.030.43±0.030.50±0.03TwistT/10CM21±1.519±1.016±1.0Dip Pick Up%4.2±1.24.2±1.24.2±1.2Elongation At Break%20±220±220±2Moisture Content%MAX 0.8MAX 0.8MAX 0.8Heat Shrinkage%MAX 4.0MAX 4.0MAX 4.0Fabric WidthCMM±2M±2M±2