硅石砖

Features: 1) Silica bricks JG - 94A for coke oven (carbide chamber):a) SiO (%): 94b) Refractoriness (SK): 31c) Porosity (%): 22d) True specific gravity: 2.34e) Cold crushing strength (MPa): 29.4f) 0.2MPa refractoriness under load (KD) (oC): 1,650g) Silica bricks JG - 94B for coke 450oC x 2Hrs (%): 0.2 2) Silica bricks for oven (other) :a) SiO (%): 94b) Refractoriness (SK): 31c) Porosity (%): 24d) True specific gravity: 2.34e) Cold crushing strength (MPa): 19.6f) 0.2MPa refractory under load (KD) (oC): 1,650g) Reheat liner change, 1,450oC x 2Hrs (%): 0.2 3) Silica bricks RG - 94 for blast furnace stoves:a) SiO (%): 94b) Fe2O3 (%): 1.5c) Al2O3 (%): 1.0d) Refractoriness (SK): 32e) Porosity (%): 23f) True specific gravity: 2.34g) Cold crushing strength (MPa): 35h) 0.2MPa refractory under load (KD) (oC): 1,650i) Reheat liner change, 1,450oC x 2Hrs (%): 0.5j) Thermal expansion at 1,000oC (%): 1.25k) 0.2MPa creep, 1,550oC x 50hrs (%): 0.8 4) Light silica bricks GGR - 1.15 (PSB) for blast furnace stoves:a) SiO (%) : 90b) Refractoriness (SK): 30c) Porosity (%): 50d) Cold crushing strength (MPa): 5e) Reheat liner change, 1,450oC x 2Hrs (%): 0.5f) Thermal expansion at 1,000oC (%): 1.30 5) Silica bricks BG - 96 for glass smelting furnace:a) SiO (%): 96b) Fe2O3 (%): 1.5c) Al2O3 (%): 0.7d) CaO (%): 2.2e) K2O + Na2O (%): 0.11f) Al2O3 + 2 (K2O + Na2O) (%): 0.5g) Refractoriness (SK): 32h) Porosity (%): 21i) True specific gravity: 2.33j) Cold crushing strength (MPa): 35k) 0.2MPa refractory under load (KD) (oC): 1,680