Полиамид 66 25% GF - огнестойких

ORACLE TM 60F30G-L is a 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties. TEST ITEMSTEST METHOD AND CONDITIONSTEST RESULTSTEST METHODUNITCONTITIONS(DRY)23DensityISO1183g/cm31.34Melt Volume RateISO1133cc/10min(275)2.16kg15Tensile StrengthISO527MPa10mm/min120Tensile strain at breakISO527%3Flexural StrengthISO178MPa180Flexural ModulusISO178MPa8,000Charpy NotchedISO179KJ/m22.9m/s-1J13Izod Notched ImpactISO180KJ/m23.5m/s-1J11.5Flame resistanceUL-94V-0Ash content%25Processing GuidelinesMaterial Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficientTypical Profile Melt Temperature 270-305 °C (518-581 °F) Mold Temperature 70-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate