H06-2 эпоксидной цинка богатые семинар Грунтовка Краска (два сопредседателя

H06-2 Epoxy Zinc Rich workshop Primer Paint (two component) Product description ØThis is epoxy polyamide adduct primer. ØA, B two component packaged. ØExcellent Performance of cathode protecting, hard film, hard wearing, antirust. ØDont influence the welding performance when the burn area is small and the film is in stated range. ØExcellent adhesive attraction, excellent oil and water resistance. Recommended uses Antirust primer for ship manufacture, steel after ball blasting or sand blasting. The maintains period can lasting for 9 12 months. Physical parameter ColorGray Gloss Matt Theoretic coverage120g/ Specific gravityAbout 2.30 Desiccation time23±2: surface dryness≤5min, Actual dryness≤24h Absolute solidification23±2: 7 days Flash pointA component: 24, B component :27 Storage12 months Operation description Mixing ratioA (paint): B (curing agent) = 35:3.5 Curing time23±2: 0.5 1 hour Applicable time23±2: 8 hours ThinnerX-7 epoxy paint thinner Operation methodAirless spraying Air spraying Manual brushing /Roller coat Max capacity of dilution20%20%5%Spout size0.4-0.5mm2.0-2.5mm-Spray pressure15-20Mpa0.3-0.6Mpa-Tool cleaningX-7 epoxy paint thinnerFilm thicknessWet film: 80um Dry film: 40um AttentionØ High zinc power contained. Suggest to mix around A component fully with machine, then put in the B component. Ø Adding thinner to avoid unable to spray caused by high temperature. Ø Zinc rich primer usually forms zinc salt. Eliminating zinc salt of the primer surface before operating subsequent paints. Or it will affect ply adhesion. Ø Avoid breath solvent vapor long time. Forbidden touching eyes and skin. Supply strong ventilation under narrow or unventilated condition. Protector is necessary. Packing specificationsA: 35kg in 20L container, B: 3.5kg in 4L container epoxy paint, anti rust coating, zinc coating